Palma

Milled during tanning creates a fabulous natural tipped grain achived in the drums.

Wonderful contrasts in colour and tipped effect within the hide offers a 'manly' look that may be used for various applications whether it be a travel bag, or a wing chair.

A strong and durable leather which will continue to burnish and polish over time.

Content Full Grain, Raised Natural Grain
Finish Aniline, Oil Pull Up
Raw Material European
Average Hide Size 50 FT2
Clean Soft Cleaner
Protection Protection Cream
Rejuvenate Oleosa

 

Leather is a natural product. Distinctive markings and nuances in its texture and colour are natural in occurrence and a testatment to its authenticity. 

Cuttings for approval (CFAs) are recommended for this leather. Expect slight color variation from dye lot to dye lot.

NOTE: Due to color variations on different monitors and color printers, before making exact color and texture matches, we recommend that you request an actual sample to ensure proper color representation as many monitors cannot display colors accuractly. CTL Leather is not responsible for color selections made from this website.

available COLOURS

Property Test Method Result
Average Thickness ISO 2589 1.4 - 1.6mm
Tensile Strength ISO 3376 Min 12 N (35-70%)
Elongation at Break ISO 3376 40 - 70%
Tear Strength ISO 3377 >70 N/mm
Flexing Endurance (after 20,000 flex) ISO 5402 No Damage
Color Fastness to Artificial Light (Xenotest 72hrs) ISO 105 B02 3-4 (Grey Scale)
Color Fastness to Rubbing (50 Dry Rubs, 20 Wet Rubs) ISO 11640 5 (Blue Scale)
Color Fastness to Rubbing (20 Sweat) ISO 11640 Min 4 (Grey Scale)
Finishing Adhesion ISO 11644 2.5 N/cm
Ignitability BS 5852-0 (Cigarette) BS 5852:1979 Pass
Ignitability BS 5852-1 (Match) BS EN 1021-1-2:2006 Pass
California Technical Bulletin 117 Cal Tech Bulletin 117-2013 Class 1
Cigarette Ignition Resistance UFAC/NFPA 260 Class 1
Boston Fire Dept BFD IX-I Pass
Wyzenbeek (Oscillatory Cylinder Method) @ 100,000 cycles ASTM D 4157.07 Pass